Steelcoat Finish P445
COATIX Steelcoat Finish P445
(Aliphatic Acrylic Polyurethane Finish Paint)
Aliphatic acrylic polyurethane tar-based, two-component, high solids, glossy topcoat paint. It is used as a final coat of paint on buildings exposed to atmospheric conditions. It has excellent adhesion, UV stability, elasticity and permanent shine. It does not wrap and has high mechanical stability. It has good chemical resistance.
• In metal structures, bridges, warehouses, factories
• On the outer surfaces of storage tanks and pipes
• On ship superstructures • In industrial and port facilities
• In oil refining and chemical plants
• As a protective coating on concrete surfaces
• It is used as a top coat in facilities exposed to the sun and outdoor weather conditions, where high color and gloss durability is required.
| Brightness (GU 60°) | Bright (85–95) |
| Color | Manufactured according to RAL codes |
| Density | 1,25 ± 0,10 g/ml |
| Hardener ratio | 80/20 by weight |
| Application viscosity | 18–25 sec / DINCUP4 / 20 °C |
| Diluent | Coatix Thinner P400 |
| Solids ratio | 50 ± 2 % by volume |
| Life of the mixture | 2 hours / 20 °C |
| Flash point | > 27 °C |
| Application method | Air spray, airless spray, roller |
| Installation period | Dusting: 20 min at 20 °C / Touching: 60 min at 20 °C / Installation: 8 hours at 20 °C |
|
Dry film thickness
|
50 μm |
| Wet film thickness | 100 μm |
| Theoretical spread | 10–11 m²/liter (for 50 μm) |